Enhancing the Mechanical Properties of Polymer-Stabilized Rammed Earth Construction
Construction materials, Vol.3(4), pp.377-388
10/17/2023
Metrics
100 Record Views
Abstract
This paper investigates the viability of using a commercially available liquid polymer (LP) in lieu of ordinary cement to stabilize soil during rammed earth (RE) construction. The scope of this study includes modifying and testing the locally available natural soil with two different LPs at various percentages. Once the optimum moisture content (OMC) of the soil with LPs was determined using the Proctor test, test samples were prepared by chemical and mechanical stabilizations. Following the curing process in an unconfined open-air laboratory environment for 7 days, soil samples were tested to determine the unconfined compressive strength (UCS) and California bearing ratio (CBR) values. The results demonstrate that the lubrication effect of polymers is different than that of water. The first polymer type yields a lower OMC compared to water, while the second polymer achieves a higher OMC. The CBR and UCS values of polymer-stabilized soils are improved for both polymer types at all dosages. The CBR values of polymer-modified soils showed as high as a 10-times improvement compared to Portland cement (PC) stabilization. A similar trend is observed for the UCS results as well. The UCS value of polymer-stabilized soils reached over 1900 psi (13 MPa), which was over 3-times higher than the UCS of PC-stabilized soil.
Related links
Details
- Title
- Enhancing the Mechanical Properties of Polymer-Stabilized Rammed Earth Construction
- Publication Details
- Construction materials, Vol.3(4), pp.377-388
- Resource Type
- Journal article
- Format
- link
- Copyright
- All articles published by MDPI are made immediately available worldwide under an open access license. No special permission is required to reuse all or part of the article published by MDPI, including figures and tables. For articles published under an open access Creative Common CC BY license, any part of the article may be reused without permission provided that the original article is clearly cited. For more information, please refer to https://www.mdpi.com/openaccess.
- Identifiers
- 99380469396006600
- Academic Unit
- Mechanical Engineering; Hal Marcus College of Science and Engineering
- Language
- English